ABOUT PRODUCT

Description

Lower shrinkage
High strength and rigidity
Carbon fiber reinforced

PAHT K7CF is a PA6-based carbon fiber reinforced nylon consumable with high strength and rigidity. Printed parts are capable of over 100 MPa’s tensile strengths (140 MPa under optimum printer and printing setup), and their continuous operating temperatures reach up to 150°C. With these properties, they are applicable to wear-resistance or high-strength parts in automobiles or machinery, and can replace metal parts in multiple applications. It is recommended to use nozzles made of wear-resistant materials.

Technical Specifications

• Material Type

          FDM PA6

• Recommended Extrusion Temperature

          270°C-300°C

• Build Platform Temperature

          90°C-110°C

• Tolerance

          ± 0.03 mm 

• Net Weight

          0.5KG/ 1KG/ 3KG per Spool